Our Practical broadswords are all based on authentically styled swords in our collection but they are tailored to meet the needs of re-enactment and stage combat. These very popular and affordable weapons feature authentic hilt styling, with fully tempered un-edged and un-pointed blades. They are designed to withstand rugged use while providing the level of safety required by many of today’s re-enactment societies. The blades are crafted from 1566 high-carbon steel, hardened to 50HRC, which restricts edge-notching to acceptable levels while providing resilience and protection against brittleness. While the blades are substantial, they are fullered to provide balance and good handling characteristics. They feature 1/16” wide edges and rounded tips for safety. The tangs are also substantial, with radiused corners at the blade shoulders and no welds. The end of the tang is riveted over the pommel, which both eliminates any possibility of inadvertent disassembly. The hardwood grips are leather-covered. The scabbards are fabricated in glass-filled resin, to eliminate swelling and to minimize blade corrosion problems, with belt rings that adjust to allow vertical or horizontal carry. The wood-grain finish is attractive, but most re-enactors will decorate the scabbard to match their persona. The Practical Single-Hand Sword is based on the Marshall sword, so named for one of England’s finest knights of the latter half of the 12th century. The sword is classically styled, with a cruciform hilt, wheel pommel and a ridged-and-fullered blade that is both stiff and surprisingly light. With a weight of less than 2 ½ lbs., the sword can be wielded forcefully without undue wear and tear on the arm.
Overall: 36 1/2“, 92cm
Blade Length: 30“, 75.5cm
Handle Length: 6 1/2”, 16.5cm
Point of Balance : 11cm
Specs will vary slightly
from piece to piece.
A high-carbon and manganese spring steel used by Hanwei in many of their differentially hardened Japanese swords and through-hardened medieval swords. This deep hardening steel provides a consistent microstructure ensuring a long life and excellent edge holding in demanding applications.
1566 Steel Composition: 0.6-0.7C 0.85-1.15Mn